Description
5754 Aluminium Sheet is a magnesium-aluminum alloy sheet with good corrosion resistance and formability. It is commonly used in structural components such as ships, automobiles, building exteriors, and storage tanks that require both corrosion resistance and strength.
Customizable content
| Customizable Item | Available Options / Ranges |
|---|---|
| Aluminium Alloy Grade | 5754 |
| Temper / Hardness | F / O / H12 / H16 / H19 / H28 / H32 / H34 / H36 / H38 / H111 / H112 / H114 / H116 / H321 |
| Thickness (mm) | 0.1–0.5 / 0.5–2 / 2–6 / 6–50 / 50–500 |
| Width (mm) | 20–500 / 500–1000 / 1000–1500 / 1500–2000 / 2000–2650 |
| Length (mm) | 100–1000 / 1000–2000 / 2000–5000 / 5000–12000 / Custom lengths |
| Sheet Form | Coil / Plate / Cut-to-size sheet |
| Surface Finish | Mill finish / Brushed finish / Coated or Painted |
| Edge Treatment | Straight edge / Deburred / Chamfered |
| Packaging Method | Coil / Carton-packed sheets / Pallet-bound sheets |
Specifications of 5754 Aluminium Sheet
| Aluminium | 5754 |
| Material temper | F, O, H12, H16, H19, H28, H32, H34, H36, H38, H111, H112, H114, H116, H321 |
| Thickness (mm) | 0.1-500 |
| Width (mm) | 20-2650 |
| Length (mm) | Customized |
Chemical Composition of 5754 Aluminum Sheet
| Elements | Si | Fe | Cu | Mn | Mg | Zn | Cr | Others | Al |
| Content | 0.4 | 0.4 | 0.1 | 0.5 | 2.6～3.6 | 0.2 | 0.3 | 0.05 | Remain |
Mechanical Properties and Tempers of 5754 Aluminium Sheet
| Aluminium Temper | Specified thickness | Tensile strength (MPa) | Yield strength (MPa) | Elongation (%) |
| H111-H38 | 0.2-50mm | 173-269 | 66-211 | 4-19 |
FAQ
Q: What processing techniques are suitable for 5754 aluminum sheet?
A: Suitable for conventional processing such as bending, stamping, welding, stretching, and cutting. The appropriate process can be selected based on the sheet thickness and condition.
Q: How to choose sheet thicknesses?
A: Thin sheets (0.1–2mm) are suitable for stamping parts or coverings; medium-thick sheets (2–50mm) are suitable for structural parts; extra-thick sheets (50–500mm) are suitable for load-bearing or large components.
Q: How does sheet condition affect its use?
A: Lower hardness conditions (F, O) are easier to form; higher hardness conditions (H series) are suitable for load-bearing or structural parts processing. Selection needs to be based on process and strength requirements.
Q: What precautions should be taken during transportation and on-site storage?
A: Rolls should be stored upright or in rolls. Sheets should be stacked flat with corners supported to avoid scratches, bending, and the effects of humid environments.
Q: How to extend the lifespan of sheet materials during processing and use?
A: Keep the surface clean, avoid scratches from sharp objects, store flat, and prevent heavy pressure or bending. Clean and treat regularly for corrosion in high humidity or coastal environments.
Hot Tags: 5754 aluminium sheet, China 5754 aluminium sheet manufacturers, suppliers, factory, aluminium legering 1050, 5251 aluminium plate for industry, 5083 alu, , Industrial iron plate, Engraved 5005 aluminum plate